To be able to keep short delivery times, we have a selection of materials we primarily work with, here we list what we offer at the moment.
Of these, below are the materials we keep in stock for extra fast delivery:
Construction steel 1.0507 (SS212, S355JS)
Hardened steel 1.6582 (SS2541, 34CrNiMo6)
Aluminum EN AW 6082 T6 (SS4212)
Steel
Construction steel 1.0507 (SS212, S355JS)
Hardened steel used for machine parts with high strength Steel used for machine components with moderate stress can be surface hardened by set hardening or nitriding to obtain a more durable surface.
Composition (%)
Material
C
Si
Mn
P
S
Cr
Ni
Mo
Other
1.0570
≤0,20
0,3
1,3
≤0,050
≤0,0050
≤0,3
–
–
Cu ≤ 0,4; n ≤ 0,009
Mechanical properties
Material
Rp0,2 (Mpa)
Rm (Mpa)
A5 min (%)
Hardness (HB)
1.0570
285
450-630
17
150-190
Machine steel 1.1201 (SS1672, C45E)
Steel used in its natural state for machine components with moderate stress, can be toughened to moderate depth, can also be induction / flame hardened to obtain a higher surface hardness for a more durable surface.
Composition (%)
Material
C
Si
Mn
P
S
Cr
Ni
Mo
Other
1.1201
0,46
≤ 0,40
0,65
≤ 0,035
≤ 0,035
–
–
–
Cr+Mo+Ni ≤ 0,63
Mechanical properties
Material
Rp0,2 (Mpa)
Rm (Mpa)
A5 min (%)
Hardness (HB)
1.1201
280
590-740
14
165-220
Toughened steel 1.6582 (SS2541, 34CrNiMo6)
Toughened steel used for machine parts with high strength requirements. High yield strength and good toughness. The steel does not need to be finished.
Composition (%)
Material
C
Si
Mn
P
S
Cr
Ni
Mo
Other
34CrNiMo6
0,36
0,25
0,65
≤ 0,035
≤ 0,035
1,5
1,5
0,23
Mechanical properties
Material
Rp0,2 (Mpa)
Rm (Mpa)
A5 min (%)
Hardness (HB)
34CrNiMo6
≤ 700
900-1100
12
–
Tool steel 1.2363 (SS2260, X100CrMoV5, AISI A2)
Medium alloy tool steel with high wear resistance and medium toughness. Often used in tool applications where the part works in a cold state. Can be cured in air / shielding gas with good dimensional stability to obtain a high surface hardness that creates a good abrasion resistance.
Composition (%)
Material
C
Si
Mn
P
S
Cr
Ni
Mo
Other
1.2363
1
0,3
0,5
5,3
1,1
–
0,2
–
Mechanical properties
Material
Rp0,2 (Mpa)
Rm (Mpa)
A5 min (%)
Hardness (HB)
1.2363
–
–
–
< 240
Aluminum
EN AW 6082 T6 (SS4212)
A high-strength aluminum for details that require the higher strength, not suitable for details that are to be anodized for decoration.
Composition (%)
Material
Si
Fe
Cu
Mn
Mg
Cr
Zn
Ti
Al
EN AW 6082 T6
1,00
0,50
0,10
0,70
0,90
0,25
0,20
0,10
Rest
Mechanical properties
Material
Rp0,2 (Mpa)
Rm (Mpa)
A5 min (%)
EN AW 6082 T6
240
280
6
EN AW 6063 T6 /6060 T6
An aluminum with a lower strength but good anodizability, suitable for applications with low stress but where the possibility of a fine surface coating is important.